USC scientists follow the bouncing metallic glass
The revolutionary material is incredibly hard but also elastic, making it potentially useful for things from drill bits to body armor to meteor-resistant casings for satellites
Engineers have created a new material with an unusual chemical structure that makes it incredibly hard and yet elastic.
The material can withstand heavy impacts without deforming even when pushed beyond its elastic limits, it doesnt fracture, instead retaining most of its original strength. That makes it potentially useful in a variety of applications from drill bits to body armor for soldiers to meteor-resistant casings for satellites.
In the journal Nature Scientific Reports, researchers from USC, the University of California, San Diego and the California Institute of Technology announced the creation of the material, which was produced by heating a powdered iron composite up to exactly 630 degrees Centigrade (1166 degrees Faherenheit) and then rapidly cooling it.
In particular, the fact that the new materials performed so well under shock loading was very encouraging and should lead to plenty of future research opportunities, said Veronica Eliasson, lead author of the paper and assistant professor at the USC Viterbi School of Engineering.
Bulk metallic glass explained
Dubbed SAM2X5-630, the new material has the highest impact resistance of any bulk metallic glass a class of artificially generated materials first discovered in the 1960s that possess disproportionate strength, resilience and elasticity due to their unusual chemical structure.
Typical metals and metal alloys have an organized, crystalline structure at the atomic level. Bulk metal glasses (BMGs, for short) are formed when metal and metal alloys are subjected to extreme heat and then rapidly cooled exciting their atoms into disorganized arrangements and then freezing them there.
In general, BMGs tend to be strong, resist scratching, tough to fracture and highly elastic. One commercially available zirconium-based BMG is pound-for-pound twice as strong as titanium.
Thanks to Professor Eliassons expertise in shocks and high-velocity testing, we were able to observe the remarkable elastic limit of this material at high velocities, a behavior which was not evident from conventional mechanical tests, said Andrea Hodge, principle investigator of the project and professor at USC Viterbi.
What makes SAM2X5-630 special is that its not entirely a glass just mostly. For some reason, the exact timing and temperatures used to create it leave just a few hints of structure here and there, which seems to be the key to its unique nature. The exact same iron composite heated and cooled slightly differently yields a completely random atomic arrangement that lacks the impressive elastic properties.
It has almost no internal structure, like glass, but you see tiny regions of crystallization, Eliasson said. We have no idea why a small amount of crystalline regions in these bulk metallic glasses makes such a big difference under shock loading.
Superheat but dont liquefy it
The Hugoniot Elastic Limit (the maximum shock it can take without irreversibly deforming) of a 1.5-1.8 mm-thick piece of SAM2X5-630 was measured at 11.76 ± 1.26 GPa.
For reference, stainless steel has an elastic limit of 0.2 GPa, while that of tungsten carbide (a high-strength ceramic used in military armor) is 4.5 GPa.
The material was produced at UC San Diego using a spark-plasma sintering process in which the iron compound is powdered, placed in a dye and then zapped with a current superheating it to the point of binding without ever liquefying it.
Eliasson and Hodge collaborated with former PhD student Gauri Khanolkar of USC, Michael Rauls of Caltech and James Kelly and Olivia Graeve of the Jacobs School of Engineering at UC San Diego.
The research was supported by the Defense Threat Reduction Agency (grant HDTRA1-11-1-0067).